by Mike - Alumilite » Wed Sep 23, 2015 6:11 am
Couple thoughts ... couple questions:
Was the tail kind of crumbly or look like it was porous where it tore? If it had too much air entrapped into it, yes ... maybe ... it could have torn from being held in a crimped position. If it was completely dense (no air bubbles or porosity in it), it should not have torn like that. The material is practically indestructible once mixed and fully cured. Wondering if someone we introduced or trapped some air into while mixing that caused some problems.
Was it only one tail that gave you problems. I'm assuming you made more than 1. Was there anything different about that one?
Mike